Assessment of thermocycling effect on mechanical properties of dental nano-composite. Modares Mechanical Engineering. 2013; 13 (3) :1-9
URL: http://journals.modares.ac.ir/article-15-10415-en.html
Abstract:   (3439 Views)
In this study the effect of thermocycling on the mechanical properties of a commercial dental nano-composite (Filtek Z350 XT, 3M ESPE, Germany) was investigated by using the nano-indentation experiment. For this purpose some disk specimens, each of the diameter 10 mm and the thickness 4 mm were prepared. Half of the specimens were stored at room temperature and the other half were thermocycled in distilled water for 1000 cycles between temperatures 5°C and 55°C. After the sample preparation, the nano-indentation test was applied on both non-themocycled and thermocycled specimens by Triboscope setup. Then the modulus of elasticity and hardness of the test samples were calculated from the Oliver-Pharr’s method using the data obtained from the nano-indentation experiments. Using the independent-samples t-test, the mechanical properties obtained from the non-thermocycled and thermocycled samples were compared. The results indicate that thermocycling process increases the modulus of elasticity and hardness of the dental nano-composite.
Full-Text [PDF 1187 kb]   (2421 Downloads)    
Article Type: Research Article | Subject: Elasticity & Plasticity|Characterization, Analysis & Selection of Materials|Micro & Nano Systems
Received: 2012/09/26 | Accepted: 2012/11/27 | Published: 2013/03/20

Add your comments about this article : Your username or Email:
CAPTCHA