Salemi A, Abdollah , A, Mirzaee M. An Investigation on Mechanical Properties of 42CrMo4 Steel with Tempered Martensite and Ferrite-Bainite-Martensite Microstructure. Modares Mechanical Engineering. 2010; 10 (1) :63-76
URL: http://journals.modares.ac.ir/article-15-8044-en.html
1- , Islamic Azad university-Karaj Branch
2- Tarbiat Modaress University
3- Tarbiat Modaress University, Tehran
Abstract:   (6512 Views)
This study is concerned with a correlation between the microstructure and mechanical properties of 42CrMo4 steel which was subjected quenched-tempered and step-quenching heat treatment. Quench tempering and step quenching heat treatment produced a tempered martensite and an equiaxed Ferrite-Bainite-Martensite (F-B-M) microstructure, respectively. Tensile test results indicated a yield drop effect in F-B-M microstructure with ferritic matrix. This effect was not observed on the specimens with tempered martensite and F-B-M microstructure with hard phase B-M matrix. This effect can be attributed to dislocation generation in ferrite phase during bainitic and martensitic transformations. Fractographic investigations indicated intergranular cleavage in F-B-M microstructure and micro-void coalescence in tempered martensite microstructure can be attributed to carbide formation in martensitic structure during tempering micro-void coalescence in tempered martensite microstructure
Full-Text [PDF 4140 kb]   (6809 Downloads)    