TY - JOUR T1 - Fabrication of hybrid nanocomposite Al2024/Gr/ZrO2 via FSP and evaluation effect role of hybrid ratio in mechanical and wear properties TT - تولید نانو کامپوزیت ترکیبی Al2024/Gr/ZrO2 توسط فرآوری اصطکاکی اغتشاشی و بررسی اثر نسبت ترکیبی بر خواص مکانیکی و سایشی JF - mdrsjrns JO - mdrsjrns VL - 16 IS - 6 UR - http://mme.modares.ac.ir/article-15-3493-en.html Y1 - 2016 SP - 119 EP - 126 KW - Friction stir processing KW - Hybrid nanocomposite KW - Mechanical Properties KW - Al 2024 N2 - Hybrid ratio of each reinforcement phases in hybrid composite can be defined as proportion of its volume to total reinforcement volume of the composite. The hybrid ratio is an important factor which controls the participation extent of each reinforcement phases in overall properties of hybrid composites. Hence, in the present work, surface hybrid nano composites of Al2024, Graphite average particle size of 100 μm and ZrO2 average particle size of 15 with different. For fabrication of nano composite the tool rotation rate was set to be 1000 rpm, and its advancing speed was 20 mm/min and tilt angle of 3 degree were chosen and all samples were subjected to 2 passes of FSP to obtain more homogeneous dispersion of the reinforcements. Subsequently, effect of hybrid ratio on microstructural, mechanical and tribological properties investigated. Optical microscopy and scanning electron microscopy were utilized to perform microstructural observation on the samples showed that reinforcements are well dispersed inside the Nugget Zone. Hardness value measurements and pin on disk dry sliding wear tests were carried out to investigate effect of hybrid ratio on mechanical and tribological properties of the nano composites. M3 ER -